CLASSIFICATION | |||||||||||||||||||
AWS A5.29 E81T1-K2C EN ISO 17632-A-T 46 6 1.5Ni P C1 1 H5
| |||||||||||||||||||
DESCRIPTION | |||||||||||||||||||
NT·E81K2 a titania type flux-cored wire, is designed for welding 560N/mm2high tensile steel for low temperatures. The weld metal contains about 1.5%-Ni and makes good notch toughness at temperatures down to -60℃under as-welded condition.It provides excellent usability with stable arc and efficiency in all-position welding. | |||||||||||||||||||
APPLICATIONS | |||||||||||||||||||
It is suitable for butt or fillet welding of offshore structures for low-temperature districts, LNG and LPG carriers, and storage tanks, etc. | |||||||||||||||||||
CURRENT TYPE | DC(+) polarity | PROCESS | 100%CO2 | ||||||||||||||||
WELDING POSITIONS | Flat, fillet, tilt, vertical up , vertical down | ||||||||||||||||||
CHEMICAL COMPOSITION OF WELDED METAL % | |||||||||||||||||||
Item | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | ||||||||||
Guarantee value | ≦0.15 | 0.5-1.75 | ≦0.80 | - | 1.00-2.00 | - | ≤0.030 | ≤0.030 | - | ||||||||||
Example value | 0.04 | 1.08 | 0.26 | - | 1.5 | - | 0.013 | 0.006 | - | ||||||||||
MECHANICAL PROPERTIES OF WELDED METAL | |||||||||||||||||||
Item | Rel/Rp0.2（MPa） | Rm（MPa） | A（%） | TEMP（℃） | KV2(J) | ||||||||||||||
GB/T Standard | ≧470 | 550-690 | ≥19 | -40 | ≥27 | ||||||||||||||
Typical values | 565 | 615 | 27 | 100 | |||||||||||||||
OPERATING CONDITIONS | |||||||||||||||||||
Diameter [mm] | Φ0.8 | Φ1.0 | Φ1.2 | ||||||||||||||||
Current [A] | Flat | 70-150 | 120-200 | 140-220 | |||||||||||||||
V-Up&Overhead | 70-140 | 110-180 | 130-200 | ||||||||||||||||
Vertical Downward | 70-150 | 120-190 | 140-210 | ||||||||||||||||
PACKAGING | |||||||||||||||||||
5kg 15kg Coil Other packaging and other diameters: please consult us | |||||||||||||||||||
CLASSIFICATION | |||||||||||||||||||
AWS A5.29 E81T1-K2C EN ISO 17632-A-T 46 6 1.5Ni P C1 1 H5
| |||||||||||||||||||
DESCRIPTION | |||||||||||||||||||
NT·E81K2 a titania type flux-cored wire, is designed for welding 560N/mm2high tensile steel for low temperatures. The weld metal contains about 1.5%-Ni and makes good notch toughness at temperatures down to -60℃under as-welded condition.It provides excellent usability with stable arc and efficiency in all-position welding. | |||||||||||||||||||
APPLICATIONS | |||||||||||||||||||
It is suitable for butt or fillet welding of offshore structures for low-temperature districts, LNG and LPG carriers, and storage tanks, etc. | |||||||||||||||||||
CURRENT TYPE | DC(+) polarity | PROCESS | 100%CO2 | ||||||||||||||||
WELDING POSITIONS | Flat, fillet, tilt, vertical up , vertical down | ||||||||||||||||||
CHEMICAL COMPOSITION OF WELDED METAL % | |||||||||||||||||||
Item | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | ||||||||||
Guarantee value | ≦0.15 | 0.5-1.75 | ≦0.80 | - | 1.00-2.00 | - | ≤0.030 | ≤0.030 | - | ||||||||||
Example value | 0.04 | 1.08 | 0.26 | - | 1.5 | - | 0.013 | 0.006 | - | ||||||||||
MECHANICAL PROPERTIES OF WELDED METAL | |||||||||||||||||||
Item | Rel/Rp0.2（MPa） | Rm（MPa） | A（%） | TEMP（℃） | KV2(J) | ||||||||||||||
GB/T Standard | ≧470 | 550-690 | ≥19 | -40 | ≥27 | ||||||||||||||
Typical values | 565 | 615 | 27 | 100 | |||||||||||||||
OPERATING CONDITIONS | |||||||||||||||||||
Diameter [mm] | Φ0.8 | Φ1.0 | Φ1.2 | ||||||||||||||||
Current [A] | Flat | 70-150 | 120-200 | 140-220 | |||||||||||||||
V-Up&Overhead | 70-140 | 110-180 | 130-200 | ||||||||||||||||
Vertical Downward | 70-150 | 120-190 | 140-210 | ||||||||||||||||
PACKAGING | |||||||||||||||||||
5kg 15kg Coil Other packaging and other diameters: please consult us | |||||||||||||||||||